Spandex fiber is the abbreviation of polyurethane fiber. The trade names include Lycra (Lycra, the United States, the United Kingdom, the Netherlands, Canada, Brazil), neolon (neolon, Japan), dorlastan (dorlastan, Germany), etc. Firstly, it was successfully studied by German Bayer company in 1937, and American DuPont company began industrial production in 1959. At present, there are nearly 40 factories and seven lines of production, with a total annual output of about 100000 tons, and China's existing production capacity of about 10000 tons. Spandex is a kind of synthetic fiber, which contains more than 85 percent polyurethane.
Υπάρχουν δύο ποικιλίες ινών spandex, η μία είναι το μωσαϊκό συμπολυμερές αρωματικής διισοκυανάσης και το τμήμα πολυεστέρα που περιέχει υδροξύλιο (εφεξής καλούμενο πολυεστερικό σπάντεξ) και το άλλο είναι το μωσαϊκό συμπολυμερές αρωματικού διισοκυανικού και το τμήμα πολυαιθέρα που περιέχει υδροξύλιο (στο εξής αναφέρεται ως σπάντεξ πολυαιθέρα). Οι ίνες Spandex, οι ελαστικές ίνες πολυολεφίνης και οι ελαστικές σύνθετες ίνες αναφέρονται συλλογικά ως ελαστικές ίνες.
Συνθετική ίνα με υψηλή επιμήκυνση θραύσης (πάνω από 400 τοις εκατό ), χαμηλό συντελεστή και υψηλή ελαστικότητα ανάκτησης. Κινεζική εμπορική ονομασία ινών πολυουρεθάνης πολλαπλών μπλοκ. Γνωστή και ως ελαστική ίνα. Το Spandex έχει υψηλή επιμήκυνση (500 τοις εκατό 700 τοις εκατό ), χαμηλό μέτρο ελαστικότητας (200 τοις εκατό επιμήκυνση, 0,04 0,12 g / Dan) και υψηλή ελαστικότητα ανάκτησης (200 τοις εκατό επιμήκυνση, 95 τοις εκατό 99 τοις εκατό ). Εκτός από την υψηλή αντοχή, άλλες φυσικές και μηχανικές ιδιότητες είναι πολύ παρόμοιες με το φυσικό μετάξι λατέξ. Είναι πιο ανθεκτικό στη χημική υποβάθμιση από το σύρμα λατέξ, έχει μέτρια θερμική σταθερότητα και η θερμοκρασία μαλακώματος είναι πάνω από 200 βαθμούς. Οι περισσότερες χρωστικές και τελικές ουσίες που χρησιμοποιούνται για συνθετικές και φυσικές ίνες είναι επίσης κατάλληλες για τη βαφή και το φινίρισμα του spandex. Το Spandex είναι ανθεκτικό στον ιδρώτα, ανθεκτικό στο θαλασσινό νερό και ανθεκτικό σε διάφορους παράγοντες στεγνού καθαρισμού και στα περισσότερα αντηλιακά. Η μακροχρόνια έκθεση στο ηλιακό φως ή στο λευκαντικό χλωρίου θα εξασθενίσει επίσης, αλλά ο βαθμός εξασθένισης ποικίλλει σημαντικά ανάλογα με τον τύπο του spandex.
Spandex fiber has such high elasticity because its polymer chain is composed of low melting point and amorphous "soft" segments as the matrix and high melting point and crystalline "hard" segments embedded in it. Flexible chain segments form a certain network structure by certain cross{{0}}linking between molecular chains. Due to the small interaction force between molecular chains, they can stretch freely, resulting in large elongation. The molecular linkage force of rigid segment is relatively large, and the molecular chain will not elongate indefinitely, resulting in high resilience. Most of the cross sections of radon fiber filaments are dog bone shaped, and some filaments have smooth or serrated surfaces. The breaking strength is the lowest among all textile fibers, only 0.44 0.88cn/dtex (the strength of polyether type is higher than that of polyester type). The moisture absorption range is small, generally 0.3-1.2 percent (the moisture absorption rate of multifilament is slightly higher than that of monofilament). The heat resistance varies greatly depending on the variety. Most fibers are stored in the range of 90 150 degree for a short time, and the fibers will not be damaged. The safe ironing temperature is below 150 degree , which can be heated and wet washed. It has excellent dyeing performance and can be dyed into various colors. The dyes have strong affinity for fiber, can adapt to most kinds of dyes, and has good chemical resistance, resistance to most acid and alkali, chemicals, organic solvents, dry cleaners and bleaches, as well as resistance to sunlight and wind and snow, but not oxide, which is easy to turn yellow and reduce the strength of fiber.
Το Spandex γενικά δεν χρησιμοποιείται μόνο του, αλλά μια μικρή ποσότητα αναμιγνύεται στο ύφασμα. Αυτό το είδος ίνας έχει ιδιότητες τόσο ελαστικού όσο και ινών. Τα περισσότερα από αυτά χρησιμοποιούνται στο νήμα με πυρήνα με σπάντεξ ως νήμα πυρήνα, το οποίο ονομάζεται νήμα με ελαστικό πυρήνα. Τα κύρια χαρακτηριστικά αυτού του νήματος είναι τα εξής: πρώτον, μπορεί να αποκτήσει καλή αίσθηση και εμφάνιση στο χέρι και η εξωτερική ίνα που αποτελείται από φυσικές ίνες έχει καλή απορρόφηση υγρασίας. Δεύτερον, μόνο 1-10 τοις εκατό νήμα spandex μπορεί να παράγει υψηλής ποιότητας ελαστικό νήμα. Τρίτον, το εύρος ελέγχου του ποσοστού ελαστικότητας είναι από 10 τοις εκατό έως 20 τοις εκατό και διαφορετικές τιμές ελαστικότητας μπορούν να επιλεγούν ανάλογα με το σκοπό του προϊόντος. Είναι εύκολο να κλωστεί μετάξι 25 2500 denier διαφορετικού πάχους, επομένως χρησιμοποιείται ευρέως για την κατασκευή ελαστικών υφασμάτων, όπως κάλτσες, κάλυμμα επίπλων, ρούχα σκι, αθλητικά ρούχα, ιατρικά υφάσματα, ζώνες, εξοπλισμός Quartermaster, ελαστικά μέρη αεροδιαστημικής ρούχα κ.λπ. Καθώς οι άνθρωποι θέτουν νέες απαιτήσεις για υφάσματα, όπως ελαφρύ βάρος, άνετη εφαρμογή και απαλή υφή, η αναλογία των υφασμάτων spandex low denier στα υφάσματα από συνθετικές ίνες αυξάνεται επίσης. Χρησιμοποιείται επίσης ως στριφτό νήμα που σχηματίζεται από τον συνδυασμό σπάντεξ γυμνού μεταξιού και σπάντεξ και άλλων ινών. Χρησιμοποιείται κυρίως για όλα τα είδη πλεκτών στημονιών και πλεκτών υφασμάτων, υφαντών και ελαστικών υφασμάτων.